Enamel Resistance to Demineralization After Bracket Debonding Using Fluoride Varnish

Abstract

The aim of this study was to evaluate the elemental content and morphology of enamel subjected to demineralization cycles after bracket debonding, adhesive remnant removal, and application of a fluoride varnish. 125 bovine teeth were divided into five groups (n = 25): 1) Intact enamel; 2) Intact enamel + demineralization cycles (DC); 3) Enamel after adhesive removal; 4)Enamel after adhesive removal + DC; 5) Enamel after adhesive removal + Profluorid + DC. The weight percentages of calcium (Ca), phosphorous (P) and fluoride (F) were calculated using energy dispersive X-ray spectroscopy (EDX). Samples were observed under scanning electron microscopy (SEM). Data were analyzed using Kruskal-Wallis and Mann-Whitney test. The weight percentages of Ca and P in Group 1 were significantly higher than Groups 2, 4, and 5. The weight percentages of Ca and P in Group 2 were significantly higher than Groups 4 and 5. Group 3 presented significantly higher percentages of Ca and P than Group 4. Group 5 showed a significantly higher percentage of Ca than Group 4. The presence of F was detected in Group 5. SEM images showed more signs of demineralization in Group 4 than Group 5. Fluoride varnish application may protect enamel from demineralization after bracket debonding.